首页> 外文期刊>Revista de metalurgia >Some influences of the chemical composition upon the viscosity of synthetic slags used in continuous steel casting
【24h】

Some influences of the chemical composition upon the viscosity of synthetic slags used in continuous steel casting

机译：化学成分对连续铸钢中合成渣粘度的一些影响

获取原文
获取原文并翻译 | 示例
       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

La calidad de productos semiacabados de la colada continua esta influenciada, en gran parte, por el proceso de lubricacion de la matriz que, a su vez, esta influenciado por la viscosidad de escoria que resulta de la colada de polvos de fundicion. Este trabajo analiza la influencia de composicion quimica sobre la viscosidad de la escoria. La investigacion ha tenido como meta establecer unas correlaciones entre la viscosidad dinamica y la composicion quimica de la escoria. Para la composicion quimica se han escogido como factores variables (componentes representativos) el contenido de CaO, MgO, Al_2O_3, SiO_2 (los dos ultimos expresados por la razon Al_2O_3/SiO_2). Los ensayos sobre la viscosidad se han realizado sobre escoria a temperaturas de 1.350 deg C. El analisis de los datos se ha efectuado en los laboratorios MATLAB y se han obtenido cuatro correlaciones multiples. Los resultados se presentan tanto en forma analitica como grafica. La utilizacion de las relaciones obtenidas permite determinar la viscosidad de las escorias con un error matematico y la utilizacion de las correlaciones graficas permite establecer el area de variacion (los limites) de la viscosidad, para los componentes representativos.%The continuous cast semifinished products quality is in a major part influenced by the lubrication process from the mould, which is influenced at its turn by slag viscosity, resulted from the melting of the lubrication powders. In the paper it is analysed the chemical composition influence on slag viscosity. The research targeted establishing some correlations between the dynamic viscosity and the chemical composition of the slag. For the chemical composition it was chosen as variable factors (representative components) the contents of CaO, MgO, Al_2O_3, SiO_2 (the last two expressed through Al_2O_3/SiO_2 ratio). The experiments for viscosity were performed on slags at temperatures of 1350 deg C. Processing the data was performed in MATLAB laboratories, obtaining four (4) multiple correlations. The results are presented both in an analytical form and in a graphical form. The use of the obtained relations allows determining slag viscosity with a mathematical error, and using graphical correlations allows establishing the variation area (the limits) of viscosity to the representative components.
机译：连续铸造的半成品的质量在很大程度上受模具润滑过程的影响，而模具的润滑过程又受铸造粉末的铸造产生的炉渣粘度的影响。这项工作分析了化学成分对炉渣粘度的影响。该研究旨在建立动态粘度与炉渣化学成分之间的关​​系。对于化学组成，已选择CaO，MgO，Al_2O_3，SiO_2（以Al_2O_3 / SiO_2之比表示的最后两个）的含量作为变量因子（代表成分）。在温度为1,350摄氏度的炉渣上进行了粘度测试。在MATLAB实验室中进行了数据分析，并获得了四个多重相关性。结果以分析和图形方式呈现。使用获得的关系可以确定具有数学误差的矿渣粘度，并且使用图形相关性可以确定代表性成分的粘度变化范围（极限）。％连续铸造半成品质量模具的主要部分受模具润滑过程的影响，而模具润滑又受熔渣熔化的影响，进而影响铸渣的粘度。本文分析了化学成分对炉渣粘度的影响。该研究旨在建立动态粘度与炉渣化学成分之间的一些相关性。对于化学成分，选择CaO，MgO，Al_2O_3，SiO_2（后两者通过Al_2O_3 / SiO_2的比值表示）的含量作为变量因子（代表成分）。粘度实验是在1350摄氏度的温度下对矿渣进行的。处理数据是在MATLAB实验室中进行的，获得了四（4）个多重相关性。结果以分析形式和图形形式呈现。使用获得的关系可以确定具有数学误差的炉渣粘度，并且使用图形相关性可以确定代表成分的粘度变化范围（极限）。