首页> 外文期刊>Molecular Crystals and Liquid Crystals >High Molecular Weight PVK as an Interlayer in Green Phosphorescent OLEDs
【24h】

High Molecular Weight PVK as an Interlayer in Green Phosphorescent OLEDs

机译：高分子量PVK作为绿色磷光OLED的中间层

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Performance of high molecular weight polyvinylcarbazole (PVK) (Mn = 1,100,000) as an interlayer has been demonstrated in the green phosphorescent organic light emitting devices (PHOLEDs) using solution process. The PVK interlayer on the surface of PEDOT:PSS has a good film uniformity characteristic with homogenous low dissolution, thereby improving the charge injection in the emissive layer effectively. The performance of high molecular weight PVK interlayer was compared with the poly(2,7-(9,9-di-n-octylfluorene)-alt-(1,4-phenylene-((4-sec-butylphenyl)imino)-1,4-phenylene)) (TFB) interlayer. The maximum current and power efficiency values of 23.1cd/A, 9.8 lm/W were demonstrated using a PVK interlayer in the green PHOLED. The effect of high molecular weight PVK interlayer and the device structure by solution processing are provided with efficient and simple manufacturing.
机译：在使用溶液法的绿色磷光有机发光器件（PHOLED）中，已经证明了高分子量聚乙烯咔唑（PVK）（Mn n = 1,100,000）作为中间层的性能。 PEDOT：PSS表面上的PVK中间层具有良好的膜均匀性，且均一的低溶解性，从而有效地改善了发射层中的电荷注入。将高分子量PVK中间层的性能与聚（2,7-（9,9-二-正辛基芴）-alt-（1,4-亚苯基-（（4-仲丁基苯基）亚氨基）- 1,4-亚苯基））（TFB）中间层。使用绿色PHOLED中的PVK中间层证明了最大电流和功率效率值为23.1cd / A，9.8 lm / W。高分子量PVK中间层的效果和通过溶液处理的器件结构提供了有效而简单的制造。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号