CdS/CdTe thin films with 2.1 μm thickness were grown using R.F. magnetron sputtering in two different mixtures of Ax and O_2. The substrate was a commercially available Pilkington glass with TCO deposited. The concentration of O_2 was selected to be 0, 1 and 5 %. The crystallographic, morphological, optical and electrical properties of the as-deposited samples were compared with the ones treated with CdCl_2 and subsequently annealed at high temperature. The films morphology and crystallinity were studied by X-ray diffraction and scanning electron microscopy. X-ray diffraction shows a transition of zinc blend cubic phase to hexagonal as the oxygen content increases from 0 to 5 %. The measurements show the larger band gap and grain sizes for the films with higher oxygen content. The band gap and transmission rate of the O_2-free and oxygenated devices is different and the grains size is greatly affected by the oxygen content.
机译：使用R.F生长厚度为2.1μm的CdS / CdTe薄膜。在两种不同的Ax和O_2混合物中进行磁控溅射。衬底是可商购的具有TCO沉积的Pilkington玻璃。 O_2的浓度选择为0％，1％和5％。将所沉积样品的晶体学，形态，光学和电学性质与经CdCl_2处理并随后在高温下退火的样品进行比较。通过X射线衍射和扫描电子显微镜研究膜的形态和结晶度。 X射线衍射显示，随着氧含量从0％增至5％，锌混合立方相向六方相的转变。测量结果表明，含氧量较高的薄膜具有较大的带隙和晶粒尺寸。不含O_2和含氧器件的带隙和传输速率不同，并且氧的含量极大地影响了晶粒尺寸。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号