首页> 外文期刊>Optical Materials >Growth and characterization of the new laser crystal Nd:LuVO_4
【24h】

Growth and characterization of the new laser crystal Nd:LuVO_4

机译：新型激光晶体Nd：LuVO_4的生长与表征

获取原文
获取原文并翻译 | 示例
   

获取外文期刊封面封底 >>

       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The growth, thermal properties, Mohs hardness, density and laser properties of a new laser crystal Nd:LuVO_4 are reported. Nd:LuVO_4 crystal belongs to tetragonal system and its cell parameter was calculated: a = 7.0275, c = 6.2507 A. The measured thermal expansion coefficient are α_a = 1.7 x 10~(-6), α_b = 1.5 x 10~(-6), α_c = 9.1 x 10~(-6)/K from 50 to 300℃ along its crystallographic axes respectively. The measured specific heat value is 0.45 J g~(-1)K~(-1) at 330 K. The highest output power at 1.064 μm is 530 mW at the pumping power of 2.76 W of a laser diode (LD), slope efficiency is 23.1%, and the optical-optical conversion efficiency is 19.3%. The theoretical density of LuVO_4 and measured density of Nd:LuVO_4 are 6.260 and 6.233 g/cm~3, respectively. And its Mohs hardness is measured to be approximately 6. All these properties show Nd:LuVO_4 is crystal can be used for efficient LD pump lasers system.
机译：报告了一种新型激光晶体Nd：LuVO_4的生长，热性能，莫氏硬度，密度和激光性能。 Nd：LuVO_4晶体属于四方晶系，其晶胞参数经计算：a = 7.0275，c = 6.2507A。测得的热膨胀系数为α_a= 1.7 x 10〜（-6），α_b= 1.5 x 10〜（-6） ），从50到300℃沿其晶轴的α_c= 9.1 x 10〜（-6）/ K。在330 K时测得的比热值为0.45 J g〜（-1）K〜（-1）。在激光二极管（LD）的泵浦功率为2.76 W，斜率为1.064μm时，最高输出功率为530 mW。效率为23.1％，光-光转换效率为19.3％。 LuVO_4的理论密度和Nd：LuVO_4的测量密度分别为6.260和6.233 g / cm〜3。测得其莫氏硬度约为6。所有这些特性表明Nd：LuVO_4是晶体，可用于高效LD泵浦激光器系统。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号