首页> 外文期刊>Optical Materials >Application of Taguchi approach to optimize the sol-gel process of the quaternary Cu2ZnSnS4 with good optical properties
【24h】

Application of Taguchi approach to optimize the sol-gel process of the quaternary Cu2ZnSnS4 with good optical properties

机译：Taguchi方法的应用以优化具有良好光学性能的四元Cu2ZnSnS4的溶胶-凝胶工艺

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Present research deals with the optimal deposition parameters configuration for the synthesis of Cu2ZnSnS4 (CZTS) thin films using the sol-gel method associated to spin coating on ordinary glass substrates without sulfurization. The Taguchi design with a L9 (3(4)) orthogonal array, a signal-to-noise (S/N) ratio and an analysis of variance (ANOVA) are used to optimize the performance characteristic (optical band gap) of CZTS thin films. Four deposition parameters called factors namely the annealing temperature, the annealing time, the ratios Cut(Zn + Sn) and Zn/Sn were chosen. To conduct the tests using the Taguchi method, three levels were chosen for each factor. The effects of the deposition parameters on structural and optical properties are studied. The determination of the most significant factors of the deposition process on optical properties of as-prepared films is also done. The results showed that the significant parameters are Zn/Sn ratio and the annealing temperature by applying the Taguchi method. (C) 2016 Elsevier B.V. All rights reserved.
机译：目前的研究涉及使用溶胶-凝胶法合成Cu2ZnSnS4（CZTS）薄膜的最佳沉积参数配置，该方法与在不硫化的情况下旋涂在普通玻璃基板上有关。 Taguchi设计采用L9（3（4））正交阵列，信噪比（S / N）和方差分析（ANOVA）用于优化CZTS薄膜的性能特征（光学带隙）电影。选择了四个沉积参数，分别称为退火温度，退火时间，比例Cut（Zn + Sn）和Zn / Sn。为了使用田口方法进行测试，为每个因素选择了三个级别。研究了沉积参数对结构和光学性能的影响。还确定了沉积过程对所制备薄膜的光学性能的最重要因素。结果表明，采用Taguchi法测定的主要参数为Zn / Sn比和退火温度。 （C）2016 Elsevier B.V.保留所有权利。

著录项