首页> 外文期刊>Optical Materials >Tape casting fabrication and properties of planar waveguide YAG/Yb:YAG/YAG transparent ceramics
【24h】

Tape casting fabrication and properties of planar waveguide YAG/Yb:YAG/YAG transparent ceramics

机译：平面波导YAG / Yb：YAG / YAG透明陶瓷的流延成型及其性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Highly transparent YAG/10at.%Yb:YAGNAG planar waveguide ceramics were fabricated by the non aqueous tape casting and solid-state reactive sintering technology. The tapes are relatively homogeneous and the green body shows a dense structure without distinct interfaces after the treatment of debinding and cold isostatic pressing. YAG/10at.%Yb:YAGNAG ceramics with almost full dense structure were obtained by vacuum-sintering at 1760 degrees C for 30 h. For the mirror-polished sample with the thickness of 3.5 mm, the In-line transmittance was measured to be 83.6% at the visual wavelength of 400 nm. The diffusion distance of the Yb3+ ions was about 215 gm along the thickness direction of the ceramics. In the lasing experiments, the YAG110at.%Yb:YAGIYAG planar waveguide ceramics were end pumped by a 976 nm semiconductor diode laser and enabled efficient continuous-wave lasers, which resulted in a maximum output power of 1.6 W and a slope efficiency of 34.4% at 1030 nm. (C) 2017 Elsevier B.V. All rights reserved.
机译：通过非水流延流延和固态反应烧结技术制备了高度透明的YAG / 10at。％Yb：YAGNAG平面波导陶瓷。带材相对均匀，经过脱脂和冷等静压处理后，生坯显示出致密的结构，没有明显的界面。通过在1760摄氏度下真空烧结30小时，获得具有几乎完全致密结构的YAG / 10at。％Yb：YAGNAG陶瓷。对于厚度为3.5 mm的镜面抛光样品，在400 nm的可见光波长下测得的在线透射率为83.6％。 Yb 3+离子沿陶瓷厚度方向的扩散距离约为215gm。在激射实验中，YAG110at。％Yb：YAGIYAG平面波导陶瓷被976 nm半导体二极管激光器泵浦并启用了高效的连续波激光器，从而产生了最大输出功率1.6 W和斜率34.4％在1030 nm （C）2017 Elsevier B.V.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号