We report a successful passive Q-switching of a Tm:YLF laser operating at lambda = 1.9 mu m, using a Co2+:AgCl0.5Br0.5 saturable absorber. Approximately 200-ns long, 150 mu J pulses were obtained. Increase in pump energy resulted in repetitive pulsing, with a repetition rate approximately proportional to the pump pulse energy. Room-temperature optical transmission saturation curves measured in similar to 1-mm thick Co2+:AgCl0.5Br0.5 plates yielded a ground state absorption cross section sigma(gs) = (7.8 +/- 0.5) x 10(-18) cm(2), and an excited state absorption cross section sigma(es) = (3.3 +/- 0.3) x 10(-18) cm(2), at lambda = 1.9 mu m. The lifetime of the A(2)(F-4) second excited-state of the octahedral 0 symmetry was tau* = (0.6 +/- 0.06) ns. (C) 2016 Elsevier B.V. All rights reserved.
机译：我们报道了使用Co2 +：AgCl0.5Br0.5饱和吸收剂在λ= 1.9微米工作的Tm：YLF激光器的成功无源Q开关。获得约200 ns长的150μJ脉冲。泵浦能量的增加会导致重复脉冲，重复频率大约与泵浦脉冲能量成正比。在类似于1毫米厚的Co2 +：AgCl0.5Br0.5板中测量的室温光透射饱和曲线得出的基态吸收截面sigma（gs）=（7.8 +/- 0.5）x 10（-18）cm（ 2），在λ= 1.9微米时的激发态吸收截面sigma（es）=（3.3 +/- 0.3）x 10（-18）cm（2）。八面体0对称性的A（2）（F-4）第二激发态的寿命为tau * =（0.6 +/- 0.06）ns。 （C）2016 Elsevier B.V.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号