首页> 外文期刊>Physical review >Comment on 'Diameter dependence of ferromagnetic spin moment in Au nanocrystals'
【24h】

Comment on 'Diameter dependence of ferromagnetic spin moment in Au nanocrystals'

机译：关于“金纳米晶体中铁磁自旋矩的直径依赖性”的评论

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Recently, Hori et al. reported diameter dependence of ferromagnetism in Au nanocrystals. Their experimental results are systematic and attractive. The authors have shown that the magnetization per nanoparticle surface area decreases with increasing diameter and vanishes at a diameter about 4 nm, as shown in Fig. 6 of Ref. 1. However, in the following, I present arguments showing that their result can be, instead, an apparent behavior resulting from the false analysis of the size dependence of saturation magnetization reported in Fig. 4 of Ref. 1.
机译：最近，Hori等人。报道了金纳米晶体中铁磁性的直径依赖性。他们的实验结果是系统的和有吸引力的。作者已经表明，每纳米颗粒表面积的磁化强度随直径的增加而减小，并在直径约4 nm时消失，如参考文献6所示。但是，在下文中，我提出了一些论据，表明它们的结果可能是由对Ref。图4中报告的饱和磁化强度的尺寸依赖性的错误分析导致的一种明显的行为。 1。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号