The present work deals with investigating the influence of microwave power on mechanical properties of 20 wt.% coir reinforced high-density polyethylene (HDPE) composites. Chopped coir/HDPE composites were fabricated using various microwave power levels (360 W, 540 W, 720 W and 900 W). The XRD analysis of the specimens reveals that crystallinity index in various specimens was in the range of 79.54% to 84.59%. The specimen cured at 360 W exhibited a maximum tensile strength of 29.5 +/- 1.5 MPa, which is 28.26% greater than composite cured at 900 W (23 +/- 1.5 MPa). Flexural strength of specimen cured at 360 W was maximum (37.74 +/- 2 MPa).
机译：本工作涉及调查微波功率对20重量％的力学性能的影响。％Coir增强高密度聚乙烯（HDPE）复合材料。使用各种微波功率水平（360W，540W，720 W和900 W）制造切碎的益官/ HDPE复合材料。标本的XRD分析表明，各种样品中的结晶性指数在79.54％至84.59％的范围内。在360W下固化的样品表现出29.5 +/- 1.5MPa的最大拉伸强度，比在900W（23 +/- 1.5MPa）下固化的复合材料大的28.26％。在360W下固化的标本的抗弯强度最大（37.74 +/- 2MPa）。