首页> 外文期刊>Solid State Communications >Fabrication and characterization of suspended single-walled carbon nanotubes
【24h】

Fabrication and characterization of suspended single-walled carbon nanotubes

机译：悬浮单壁碳纳米管的制备与表征

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Suspended single-walled carbon nanotubes (SWCNTs) between SiO2 pillars via a direct lithographic route using a simple mixture of catalyst precursor [Co(III) acetylacetonate, Co(acac)(3)] and conventional electron beam resist (ma-N2403) were fabricated. The catalytic electron beam resist (Cat-ER) layer plays dual roles as a catalyst and a resist layer for the growth and alignment of CNTs, respectively. The structure of the grown nanotube was characterized by Raman spectroscopy (633 nm laser excitation). Nanotubes grown from Cat-ER with Co(acac)3 show the typical Raman spectra of SWCNTs which are characterized by the strong tangential bands near to 1590 cm(-1) and radial breathing modes (RBMs) in the low frequency region (< 300 cm(-1)). The calculated diameter of the probed nanotubes individually corresponds to the range 0.86-1.77 nm. (c) 2006 Elsevier Ltd. All rights reserved.
机译：使用催化剂前体[乙酰丙酮钴（III），钴（acac）（3）]和常规电子束抗蚀剂（ma-N2403）的简单混合物，通过直接光刻路线在SiO2柱之间悬挂单壁碳纳米管（SWCNT），捏造的。催化电子束抗蚀剂（Cat-ER）层分别充当催化剂和CNT生长和对准的抗蚀剂层。生长的纳米管的结构通过拉曼光谱法（633nm激光激发）表征。由Cat-ER与Co（acac）3合成的纳米管显示了SWCNTs的典型拉曼光谱，其特征是接近1590 cm（-1）的强切向带和低频区域（<300）的径向呼吸模式（RBM）。厘米（-1））。所探测的纳米管的计算直径分别对应于0.86-1.77 nm的范围。 （c）2006 Elsevier Ltd.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号