首页> 外文期刊>Solid State Communications >First applicability of ZnGa2O4 : Ge4+, Li+, Mn2+ phosphor for a plasma display panel
【24h】

First applicability of ZnGa2O4 : Ge4+, Li+, Mn2+ phosphor for a plasma display panel

机译：ZnGa2O4：Ge4 +，Li +，Mn2 +荧光粉的首次应用

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The green emission intensity of ZnGa2O4:Ge4+, Li+, Mn2+ excited by the vacuum ultraviolet line of 147 nm reaches 70% of commercial green Zn2SiO4:Mn2+. The vacuum ultraviolet excitation spectra consist of four peaks. In a plasma display test bed filled with Ar and Ne plasma discharged by a radio-frequency generator of 13.6 MHz, ZnGa2O4:Ge4+, Li+, Mn2+ and commercial Zn2SiO4:Mn2+ phosphor screens show a linear increase in luminance with increasing self bias voltages. Increasing gas pressures cause the luminance to increase. Also, on increasing the self bias voltages and the gas pressures, the current densities of ZnGa2O4:Ge4+, Li+, Mn2+ phosphor screens are increased; this is the same behavior as that of the commercial phosphor. (c) 2006 Elsevier Ltd. All rights reserved.
机译：由147 nm的真空紫外线激发的ZnGa2O4：Ge4 +，Li +，Mn2 +的绿色发射强度达到商品绿色Zn2SiO4：Mn2 +的70％。真空紫外激发光谱由四个峰组成。在充满13.6 MHz射频发生器放电的充有Ar和Ne等离子体的等离子显示器测试台中，ZnGa2O4：Ge4 +，Li +，Mn2 +和商用Zn2SiO4：Mn2 +荧光屏的亮度随自偏压的增加呈线性增加。气压升高会导致亮度增加。另外，随着自偏压和气压的增加，ZnGa2O4：Ge4 +，Li +，Mn2 +荧光屏的电流密度增加；这与市售磷光体的行为相同。 （c）2006 Elsevier Ltd.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号