首页> 外文期刊>Solid State Communications >Conductance and EPR study of the endohedral fullerene Li @C-60
【24h】

Conductance and EPR study of the endohedral fullerene Li @C-60

机译：内膜富勒烯@@ C-60的电导和EPR研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Thin films and bulk samples of endohedral fullerenes Li@C-60 are studied using current-voltage (I-V) measurements and electron paramagnetic resonance (EPR). Electrical measurements show a linear behaviour for the I-V curves and give an average resistivity of ca. 1.5 kOmegacm for thin Li@C-60 films deposited in vacuum, four orders of magnitude lower than C-60 samples. A drastic effect on the conductance, lowering it to the values typical for C-60, is observed when the Li@C-60 samples are exposed to ambient atmosphere. No additional paramagnetic centres (PCs) are found for the Li@C-60 compared to C-60 that can be related to the formation of dimers or trimers of the endohedral fullerene molecules. However, the presence of the Li atoms in the fullerene cages contributes to a change of the spin-spin and spin-lattice relaxation times. The spin-lattice relaxation time becomes four orders of magnitude longer compared to the spin-spin relaxation time. (C) 2004 Elsevier Ltd. All rights reserved.
机译：使用电流-电压（I-V）测量和电子顺磁共振（EPR）研究了内面富勒烯Li @ C-60的薄膜和大量样品。电气测量结果显示了I-V曲线的线性行为，并给出了平均电阻率ca。对于在真空中沉积的Li @ C-60薄膜，厚度为1.5 kOcmcm，比C-60样品低四个数量级。当Li @ C-60样品暴露于环境大气时，观察到对电导的剧烈影响，将其降低到C-60的典型值。与C-60相比，没有发现Li @ C-60的其他顺磁性中心（PC），这可能与内面富勒烯分子的二聚体或三聚体的形成有关。但是，在富勒烯笼中存在Li原子有助于改变自旋-自旋和自旋晶格的弛豫时间。与自旋-自旋弛豫时间相比，自旋-晶格弛豫时间变得更长四个数量级。 （C）2004 Elsevier Ltd.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号