首页> 外文期刊>Solid State Communications >Structure and magnetic properties of CoxPb1-x nanowire arrays
【24h】

Structure and magnetic properties of CoxPb1-x nanowire arrays

机译：CoxPb1-x纳米线阵列的结构和磁性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Ordered CoxPb1-x nanowire arrays embedded in the porous anodic aluminum oxide (AAO) template have been fabricated by electrodeposition. XRD experiments prove that neither hexagonal-close-packed (hcp) nor face-centered-cubic (fcc) Co peaks are detected when the Co component (x) is below 0.91. The coercivity (H-c) and squareness (M-x/M-s) are found to increase with ferromagnetic Co component and the maximum value is at the position x = 1 (pure Co nanowires). Annealing effects cause H-c and M-r/M-s increase, which surpasses the pure Co nanowires in the 0.2 < x < 0.6 at the annealing temperature of 700degreesC. Microstructure change during annealing process is proposed to explain the magnetic properties change of samples. (C) 2004 Elsevier Ltd. All rights reserved.
机译：通过电沉积已制备了嵌入多孔阳极氧化铝（AAO）模板中的有序CoxPb1-x纳米线阵列。 XRD实验证明，当Co分量（x）低于0.91时，既未检测到六角密堆积（hcp），也未检测到面心立方（fcc）的Co峰。发现矫顽力（H-c）和矩形度（M-x / M-s）随着铁磁Co分量的增加而增加，最大值在x = 1的位置（纯Co纳米线）。退火效应导致H-c和M-r / M-s的增加，在700摄氏度的退火温度下，其纯Co纳米线的0.2

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号