Refined Evaluation of the Remaining Service Life of Steam Line Bends by Simulating the Durability of Metal through Tests of Notched Samples

机译:通过缺口样品测试模拟金属的耐用性,细化评估蒸汽管线弯曲的剩余使用寿命

获取原文
获取原文并翻译 | 示例
           

摘要

The postulated analogy between the influence on longevity of a relatively high extent of creep-caused microdamage and initial decrease in a sample's cross section due to annular notch is used as a basis for carrying out an experimental study of the effect of temperature, stress, and loading time on the coefficient characterizing the relative residual longevity of metal after the occurrence of pore chains along the grain boundaries.
机译:假定的相对较高程度的蠕变引起的微损伤对寿命的影响与由于环形缺口引起的样品横截面初始减小之间的类比,被用作进行温度,应力和应力影响的实验研究的基础。加载时间的系数表征了沿晶界出现孔链后金属的相对剩余寿命。

著录项

  • 来源
    《Thermal engineering》 |2011年第2期|p.95-100|共6页
  • 作者

    V.I.Gladshtein;

  • 作者单位

    All-Russia Thermal Engineering Institute, ul.Avtozavodskaya 14/23, Moscow, 115280 Russia;

  • 收录信息
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号