首页> 外文期刊>Thin Solid Films >Effect of boron substitution on the properties of NiZnCu ferrite for multilayer chip inductors
【24h】

Effect of boron substitution on the properties of NiZnCu ferrite for multilayer chip inductors

机译：硼替代对多层片式电感器NiZnCu铁氧体性能的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The initial permeability of the toroidal core sample with boron substituted NiZnCu ferrite (Ni_(0.36)Zn_(0.44)Cu_(2.2)-Fe_(196_x)B_xO_4(x = 0.0, 0.2, 0.4, 0.6, and 0.8)) which was annealed at 900 ℃ for 2 h decreased from 162.4 to 123.2 as boron concentration x is increased from 0.2 to 0.8. The quality factor and density of 0.2 mol% boron substituted NiZnCu ferrites sintered at 900 ℃ for 2 h was about 240.0 and 4.84 g/cm~3, respectively. The density, shrinkage and saturation magnetization were increased with increasing annealing temperature. It was shown that the boron substituted NiZnCu ferrite systems were promising as a high quality factor material in the fabrication of multilayer chip inductors (MLCIs).
机译：硼取代的NiZnCu铁氧体（Ni_（0.36）Zn_（0.44）Cu_（2.2）-Fe_（196_x）B_xO_4（x = 0.0、0.2、0.4、0.6和0.8）退火的环形磁芯样品的初始磁导率随着硼浓度x从0.2增加到0.8，在900℃下加热2小时后从162.4降低到123.2。在900℃下烧结2 h的0.2 mol％硼取代的NiZnCu铁氧体的品质因数和密度分别约为240.0和4.84 g / cm〜3。密度，收缩率和饱和磁化强度随退火温度的升高而增加。结果表明，在多层片式电感器（MLCI）的制造中，硼取代的NiZnCu铁氧体系统有望成为一种高质量的材料。

著录项

  • 来源
    《Thin Solid Films》 |2011年第23期|p.8388-8390|共3页
  • 作者

    Sung Yong An; Ic Seob Kim; Soo Hwan Son; So Yeon Song; Jin Woo Hahn; Kang Ryong Choi; Sung Wook Hyun; Chin Mo Kim; Chul Sung Kim;

  • 作者单位

    LCR Division, Samsung Electro-Mechanics, Suwon 443-743, Republic of Korea;

    LCR Division, Samsung Electro-Mechanics, Suwon 443-743, Republic of Korea;

    LCR Division, Samsung Electro-Mechanics, Suwon 443-743, Republic of Korea;

    LCR Division, Samsung Electro-Mechanics, Suwon 443-743, Republic of Korea;

    LCR Division, Samsung Electro-Mechanics, Suwon 443-743, Republic of Korea;

    Department of Physics, POSTECH, Pohang 790-784, Republic of Korea;

    Department of Physics, Kookmin University, Seoul 136-702, Republic of Korea;

    Department of Physics, Kookmin University, Seoul 136-702, Republic of Korea;

    Department of Physics, Kookmin University, Seoul 136-702, Republic of Korea;

  • 收录信息
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类
  • 关键词

    NiZnCu ferrite; multilayer chip inductors; toroidal core;

    机译：NiZnCu铁氧体;多层片式电感器;环形磁芯;

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号