Evaluation of Surface Damage and Residual Strength in Ceramics due to Sphere Impact (2nd Report, Si3N. Sphere Impact to Si3N. Specimen--Elastic AnaIysis)

Koji OHGUSHI; Kyoji HOMMA; Masahiro ICHIKAWA

首页> 外文期刊>日本機械学会論文集. A編 >Evaluation of Surface Damage and Residual Strength in Ceramics due to Sphere Impact (2nd Report, Si3N. Sphere Impact to Si3N. Specimen--Elastic AnaIysis)

【24h】

Evaluation of Surface Damage and Residual Strength in Ceramics due to Sphere Impact (2nd Report, Si3N. Sphere Impact to Si3N. Specimen--Elastic AnaIysis)

机译：评估陶瓷由于球体撞击而造成的表面损伤和残余强度（第二份报告，Si3N。球体对Si3N的撞击。试样－弹性分析）

获取原文

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

In the 1st report, it was shown that it was possible to apply an elastic indentation theory to the evaluation of surface damage of ceramics due to sphere impact, although this was limited to low velocities in which elastic damage dominated. In this research, further investigation on the applica- bility of the theory to the residual strength evaluation was conducted. In the case that elastic damage or cone crack was related in the final fracture, the residual strength of ceramic specimens damaged by sphere impact was estimated using the elastic indentation theory and conventional fracture mechanics. Good agreement between estimated curves and test results were obtained.

机译：在第一份报告中，表明可以将弹性压痕理论应用于评估由于球体撞击而引起的陶瓷表面损伤，尽管这仅限于以弹性损伤为主的低速度。在这项研究中，对该理论在残余强度评估中的适用性进行了进一步研究。如果在最终断裂中存在弹性损伤或圆锥裂纹，则使用弹性压痕理论和常规断裂力学来估算受球体冲击破坏的陶瓷试样的残余强度。估计曲线与测试结果之间具有良好的一致性。

著录项

来源
《日本機械学会論文集. A編》 |1999年第634期|83-|共页
作者
Koji OHGUSHI; Kyoji HOMMA; Masahiro ICHIKAWA;
展开▼
作者单位

展开▼
收录信息
原文格式 PDF
正文语种 jpn
中图分类机械、仪表工业;
关键词
Ceramics; Contact Problem; Impact Strength; Residual Strength; Sphere; Silicon Nitride; Indentation; Elastic Analysis;

机译：陶瓷;联系问题;冲击强度残余强度;球;氮化硅;缩进;弹性分析;

相似文献

外文文献
专利

1. Evaluation of Surface Damage and Residual Strength in Ceramics due to Sphere Impact (3rd Report, SiC Sphere Impact to SiC Specimen) [J] . Koji OHGUSHI, Kyoji HOMMA, Masahiro ICHIKAWA 日本機械学会論文集. A編 . 1999,第634期

机译：评估陶瓷因球体撞击而造成的表面损伤和残余强度（第三次报告，SiC球体对SiC试样的撞击）
2. Evaluation of Surface Damage and Residual Strength in Ceramics due to Sphere Impact (1st Report, Si_3N_4 Sphere Impact to Si_3N_4 Specimen--Experimental Results) [J] . Koji OHGUSHI, Kyoji HOMMA, Masahiro ICHIKAWA 日本機械学会論文集. A編 . 1999,第634期

机译：评估陶瓷因球体撞击而造成的表面损伤和残余强度（第一份报告，Si_3N_4球体对Si_3N_4试样的撞击-实验结果）
3. SPHERE IMPACT INDUCED DAMAGE IN CERAMICS: II. ARMOR-GRADE B{sub}4C AND WC [J] . J. C. LaSalvia, M. J. Normandia, H. T. Miller, Ceramic Engineering and Science Proceedings . 2005,第7期

机译：球形撞击引起的陶瓷损伤：II.。装甲等级B {sub} 4C和WC
4. Evaluation of residual strength in ceramics due to sphere impact [C] . Takashi Matsumura, Yasuo Ochi, Koji Ohgushi, SEM IX International Congress on Experimental Mechanics June 5-8, 2000 Orlando, Florida . 2000

机译：评估由于球体撞击造成的陶瓷残余强度
5. Response surface characterization of impact damage and residual strength degradation in composite sandwich panels. [D] . Samarah, Issam Khder. 2003

机译：复合夹芯板冲击损伤和残余强度降低的响应面特征。
6. 2nd coordination sphere controlled electron transfer of iron hangman complexes on electrodes probed by surface enhanced vibrational spectroscopy [O] . H. K. Ly, P. Wrzolek, N. Heidary, 2015

机译：表面增强振动光谱法探测电极上金属子配合物的第二配位球控制电子转移
7. On Evaluation Method of Damage Development for CFRP Laminates under Low Impact Energy (1st Report, Estimation of Residual Strength based on Static Bending Test after Occurrence of Damage) [O] . Tetsusei KURASHIKI, Masaru ZAKO, Tokinari KEYAKIDA 2005

机译：低冲击能源CFRP层压板损伤开发的评价方法（第1次报告，基于静态弯曲试验损伤后静态弯曲试验的估计）
8. Structural Damage Prediction and Analysis for Hypervelocity Impact: Properties of Largest Fragment Produced by Hypervelocity Impact of Aluminum Spheres with Thin Aluminum Sheets [R] . Piekutowski, Andrew J. 1995

机译：超高速撞击的结构损伤预测与分析：薄铝板铝球超高速撞击产生的最大碎片性质

Evaluation of Surface Damage and Residual Strength in Ceramics due to Sphere Impact (2nd Report, Si3N. Sphere Impact to Si3N. Specimen--Elastic AnaIysis)

摘要

著录项

相似文献

相关主题

期刊订阅