The influence of permanent-magnet-driven stirring during solidification on the microstructure and corrosion property of AZ61 magnesium alloy was investigated. The corrosion behaviour of AZ61 was studied in 3.5mol/L NaCl by measuring electrochemical polarization. The results show that the permanent-magnet stirring refines the microstructure of AZ61 magnesium alloy, which improves the precipitation amount and distribution uniformity of β phase and decreases the content of hydrogen, but it has less influence on the distribution uniformity of Zn. The change of precipitation amount of β phase influences the corrosive nature of the matrix, and it has no direct proportion with the corrosion resistance of the matrix.
机译：研究了凝固过程中永磁驱动搅拌对AZ61镁合金组织和腐蚀性能的影响。通过测量电化学极化，研究了AZ61在3.5mol / L NaCl中的腐蚀行为。结果表明，永磁搅拌细化了AZ61镁合金的组织，提高了β相的析出量和分布均匀性，降低了氢含量，但对Zn的分布均匀性影响较小。 β相沉淀量的变化会影响基体的腐蚀性能，与基体的耐蚀性没有直接关系。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号