Effects of nitriding temperature on magnetic properties of melt-spun Pr_1.4Fe_10.5Mo_1.5N_x and its phase analysis

机译：氮化温度对熔纺Pr_1.4Fe_10.5Mo_1.5N_x磁性能的影响及其相分析

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The phase transition of melt-spun Pr_1.4Fe_10.5Mo_1.5 and its nitrides have been studied by means of XRD and TEM. The phases of the alloy are α-Fe(Mo) (containing a little of other phases), Pr(Fe, Mo)_12, Pr(Fe, Mo)_7, Pr(Fe, Mo)_12 and Pr(Fe, Mo)_12N_x in turn after having been arc melted in a pu- rified argon, homogenized, melt-spun, annealed and nitrided. The magnetic properties are obtained on vibrat- Ing sample magnetometer (VSM). After annealing at 760 deg. C for 30 min and nitrided at 600 deg. C for 2 h, B_r is 0.349 T and H_c is 115.4 kA·m~-1.
机译：利用XRD和TEM研究了熔纺Pr_1.4Fe_10.5Mo_1.5及其氮化物的相变。合金的相为α-Fe（Mo）（含有少量其他相），Pr（Fe，Mo）_12，Pr（Fe，Mo）_7，Pr（Fe，Mo）_12和Pr（Fe，Mo在纯氩气中电弧熔化，均质，熔融纺丝，退火和氮化后，依次得到）_12N_x。磁性是通过振动Ing样品磁强计（VSM）获得的。在760度退火后。加热30分钟并在600℃下氮化。 C为2小时，B_r为0.349T，H_c为115.4kA·m〜-1。