首页> 外文期刊>Vlakna a Textil >Polypropylene fibres modified by copolyamides Part Ⅰ. Preparation of modifed fibres and their properties
【24h】

Polypropylene fibres modified by copolyamides Part Ⅰ. Preparation of modifed fibres and their properties

机译：共聚酰胺改性的聚丙烯纤维第一部分。改性纤维的制备及其性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Tento príspevok je venovaný syntéze kopolyamidov z ε-kaprolaktámu CL a nylonovej soli ADETA z kyseliny adipovej (A) a dietyléntriamínu (DETA) a hodnoteniu niektorých ich základných vlastností. Kopolyamidy obsahujúce 5, 10 alebo 15% hm. nylonovej soli ADETA boli použité ako aditíva pre vláknotvorný PP a PP vlákna modifikované 4, 8 a 12 hm.% kopolyamidov boli pripravené. Molové hmotnosti kopolyamidov sú dostatočne vysoké na to, aby sme ich považovali za polymérne aditíva. Teploty tavenia sú nižšie v porovnaní s teplotou tavenia homopolyamidu PA6 a ich tepelná stabilita je porovnateľná s PP. Mechanické, elektrické a sorpčné vlastnosti modifikovaných PP vlákien závisia na obsahu kopolyamidu vo vlákne. Čím je vyšší obsah kopolyamidu tým nižšia je pevnosť, tým vyšší je stupeň elasticity a sorpcia vodných pár, a tým lepšie sú elektrické vlastnosti modifikovaných PP vlákien.%This contribution is devoted to the synthesis of copolyamides from ε-caprolactam (CL) and ADETA nylon salt from adipic acid (A) and dietylenetriamine (DETA) and an evaluation of some their basic characteristics. Copolyamides containing 5, 10 or 15 wt.% of ADETA nylon salt were used as additives and PP fibres modified with 4, 8 and 12 wt.% of copolyamides were prepared. The molecular weights of copolyamides are high enough to consider them as polymer additives. The melting temperatures are lower in comparison with homopolyamide PA 6 and their thermal stability is equal to that of PP. The mechanical, electric and sorptive properties of modified PP fibres depend on the amount of copolyamide in the fibre. The higher the amount of each copolyamide, the higher the degree of elasticity and sorption of water vapour. Also the electric properties are better, and the tensile strength of modified PP fibres is lower.
机译：本文致力于由ε-己内酰胺CL合成共聚酰胺，由己二酸（A）和二亚乙基三胺（DETA）合成尼龙盐ADETA及其一些基本性能的评估。含有5、10或15％重量的共聚酰胺将25％的ADETA尼龙盐用作形成纤维的PP的添加剂，并制备了用4、8和12重量％的共聚酰胺改性的PP纤维。共聚酰胺的摩尔质量足够高以被认为是聚合物添加剂。熔点比均聚酰胺PA6的熔点低，并且它们的热稳定性与PP相当。改性PP纤维的机械，电和吸附性能取决于纤维中共聚酰胺的含量。共聚酰胺含量越高，强度越低，弹性和水蒸气吸附度越高，改性PP纤维的电性能就越好。％此贡献致力于由ε-己内酰胺（CL）和ADETA尼龙合成共聚酰胺。己二酸（A）和二亚乙基三胺（DETA）中的盐及其一些基本特性的评估。将含有5、10或15重量％的ADETA尼龙盐的共聚酰胺用作添加剂，并制备经4、8和12重量％的共聚酰胺改性的PP纤维。共聚酰胺的分子量足够高，可以将其视为聚合物添加剂。与均聚酰胺PA 6相比，其熔融温度更低，并且其热稳定性与PP相同。改性PP纤维的机械，电和吸附性能取决于纤维中共聚酰胺的含量。每种共聚酰胺的量越高，水蒸气的弹性和吸附度越高。电气性能也更好，而改性PP纤维的抗张强度较低。