摘要

Creep and duration of load characteristics of cross laminated timber (CLT) were evaluated from the test results of creep and duration of tests. Japanese Ceder (Cryptomeria japonica) was chosen for the specie for the laminations of the test specimens and API was chosen for the adhesive. The results are summarized as follows:(1)The duration of load factor [i.e. Strength for 50 years duration of load / Strength for 10 minutes duration of load] of CLT was evaluated to be 0.66 and was almost equivalent to the duration of load factor measured for solid lumbers. (2) The creep factor [i.e. (Initial deflection + Creep deflection) / Initial deflection] for CLT was evaluated to be 1.2 to 2.6 and was almost equivalent to the creep factor commonly known for solid lumber.%本研究では，長期的かっ継続的に作用する荷重に対するCLTの力学的な性状に関する知見を得ることを目的として，スギ挽き板より構成されたCLTのクリープ破壊試験とクリープ試験を実施し，荷重継続時間の調整係数と変形増大係数を算出した。荷重継続時間の調整係数に関して得られた知見を以下に記す。1)平成12年建設省告示1446に示されている方法を用いて評価した荷重継続時間の調整係数は0.66であった。
机译：选择日本Ceder（Cryptomeria japonica）作为测试样品的薄片，选择API作为Creep，并根据蠕变和测试时间的测试结果评估了交叉层压木材（CLT）的载荷特性持续时间。结果总结如下：（1）CLT的负载因数持续时间[即50年负载持续时间的强度/ 10分钟负载持续时间的强度]的评估为0.66，几乎等于CLT的持续时间。 （2）CLT的蠕变系数[即（初始挠度+蠕变挠度/初始挠度）评估为1.2到2.6，几乎等于通常用于实木的蠕变系数。％在这项研究中，我们进行了由日本雪松磨床组成的CLT的蠕变断裂试验和蠕变试验，以便获得有关CLT在长期和连续载荷下的机械性能的知识，并继续载荷。计算了时间调整因子和变形增加因子。下面描述关于负载持续时间的调整因子获得的知识。 1）使用2000年建设部公告1446中所示方法评估的荷载持续时间调整系数为0.66。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号