Blends of acrylic polymer (containing acrylonitrile 91.7%, methyl acrylate 7%, and sodium methyl propenyl sulfonate 1.3% [wt %], denoted as PAC) with silk fibroin (SF) were studied in the form of drawn fibers with varied compositions. The strength, elongation, and specific work of rupture of the blend fibers decrease with increase of the SF content, whereas the modulus has a slight increase up to 20% (wt) SF and then decreases. With the addition of up to 30% (wt %) SF in the PAC matrix, the moisture absorption increases from 2.06 to 6.2% in comparison with the PAC. Scanning electron microscopy studies show that the blend fibers have a sheath-core structure, with SF mainly in the sheath and PAC in the core. FTIR, ATR, and X-ray diffraction results of the blend fibers are also presented. (C) 1997 John Wiley & Sons, Inc. [References: 19]
机译：以具有不同组成的拉伸纤维的形式研究了丙烯酸类聚合物（包含91.7％的丙烯腈，7％的丙烯酸甲酯和1.3％[wt％]的丙烯基甲基磺酸钠，以PAC表示）的共混物。共混纤维的强度，伸长率和断裂比功随SF含量的增加而降低，而模量则略有增加，直至20％（wt）SF，然后降低。与PAC相比，在PAC基质中添加高达30％（wt％）的SF时，吸湿率从2.06％增至6.2％。扫描电子显微镜研究表明，共混纤维具有皮-芯结构，SF主要位于皮中，而PAC位于芯中。还显示了混合纤维的FTIR，ATR和X射线衍射结果。 （C）1997 John Wiley＆Sons，Inc. [参考：19]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号