首页> 外文期刊>Journal of Materials Engineering and Performance >Strengthening Characteristics of Nitrogen Alloyed 201 Stainless Steel
【24h】

Strengthening Characteristics of Nitrogen Alloyed 201 Stainless Steel

机译：氮合金201不锈钢的强化特性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Strengthening characteristics of 201 stainless steel under nitrogen enhancement from zero to approximately 1.5 wt percent N concentration are improved with increasing nitrogen. Yield and tensile strength, strain hardening, and cold-work/hardness relationships are proportional to nitrogen concentration. Strengths increased with increasing nitrogen up 1,0 wt percent, even though at nitrogen concentrations greater than ?.65 wt percent, Cr_2N precipitates formed. Strengthening models from tensile and cold working are discussed, compared, and correlated to nitrogen concentration, tensile properties, and micrestructure.
机译：随着氮含量的增加，在氮含量从零提高到约1.5 wt％的情况下，201不锈钢的强化特性得到改善。屈服强度和拉伸强度，应变硬化以及冷作/硬度关系与氮浓度成正比。即使氮浓度大于≥0.65重量％，也会形成Cr_2N沉淀，但随着氮含量增加1,0重量％，强度也会增加。讨论，比较了拉伸和冷加工的强化模型，并将其与氮浓度，拉伸性能和微结构相关联。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号