Phosphate glass samples with various Cr2O3, Yb2O3, and Er2O3 contents based upon 67P(2)O(5). 14Al(2)O(3). 14Li(2)O . 1K(2)O.4(Yb2O3 + Er2O3) were prepared. The effect of changing concentrations of Er3+ ions (0.1-1.5 x 10(19) ions cm(-3)) and sensitizers Cr3+ ion and Yb3+ ion (2-16 x 10(18) ions cm(-3) and 1.35-2.3 x 10(21) ions cm(-3) respectively) on laser performance were investigated. The thermal shock resistance of this glass was doubled after an ion-exchange chemical strengthening process in a KNO3/NaNO3 molten salt bath. Lasers with repetition rates of 20 Hz at free-running and 15 Hz at Q-switched single mode were demonstrated by utilizing chemically strengthened laser glass rods. (C) 1998 Elsevier Science B.V. All rights reserved. [References: 16]
机译：基于67P（2）O（5）的具有各种Cr2O3，Yb2O3和Er2O3含量的磷酸盐玻璃样品。 14Al（2）O（3）。 14Li（2）O。制备了1K（2）O.4（Yb2O3 + Er2O3）。改变Er3 +离子（0.1-1.5 x 10（19）离子cm（-3）和敏化剂Cr3 +离子和Yb3 +离子（2-16 x 10（18）离子cm（-3）和1.35-2.3浓度）的影响x 10（21）离子cm（-3）分别对激光性能进行了研究。在KNO3 / NaNO3熔融盐浴中进行离子交换化学强化处理后，该玻璃的耐热冲击性提高了一倍。通过使用化学强化的激光玻璃棒，证明了在自由运行时重复频率为20 Hz，在Q切换单模情况下重复频率为15 Hz的激光器。 （C）1998 Elsevier Science B.V.保留所有权利。 [参考：16]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号