High strength SiO2 aerogel insulation

机译：高强度SiO2气凝胶绝缘

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Silica aerogels with titanium dioxide powder and inorganic binders were made using tetraethoxysilane (TEOS), water and HF catalyst, followed by supercritical drying with ethanol leading to crack-free monolithic aerogels. Strength of the monolithic silica aerogels increased from 1.8 X 10(4) Pa to 1.2 X 10(5) Pa with doping, while the thermal conductivity of the doped silica aerogel remains below 0.02 w/m K at room temperature in air. (C) 1998 Elsevier Science B.V. All rights reserved. [References: 5]
机译：使用四乙氧基硅烷（TEOS），水和HF催化剂制得具有二氧化钛粉末和无机粘合剂的二氧化硅气凝胶，然后用乙醇进行超临界干燥，从而制得无裂纹的整体气凝胶。掺杂后，整体式二氧化硅气凝胶的强度从1.8 X 10（4）Pa增加到1.2 X 10（5）Pa，而室温下在空气中，掺杂的二氧化硅气凝胶的热导率保持在0.02 w / m K以下。 （C）1998 Elsevier Science B.V.保留所有权利。 [参考：5]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号