Atmosphere control during ctebiading of powder Injection molded (PIM) parts is an important parameter to consider. Experimental results have shown that a stagnant atmosphere containing volatiles evolved during debinding can cause slumping of the green samples. Removal of volatiles from the sample zone aids debinding and can reduce cycle times and improve sample quality. Eesidual carbon and oxygen can be controlled during debinding by adjusting the atmosphere composition. This paper presents the results of PIM 70 vol percent spherical copper powder and 30 vol percent binder. Debinding atmospheres were altered to determine the effect of debinding on the green body and the sintered sample.
机译：粉末注射成型（PIM）零件的CTEBIAS中的气氛控制是需要考虑的重要参数。 实验结果表明，在脱脂期间含有挥发物的挥发物的停滞气氛会导致绿色样品的衰退。 从样品区除去挥发物，助剂促进逐次，可以减少循环时间并提高样品质量。 通过调节大气组合物，可以在逐渐进行eESidual碳和氧气。 本文介绍了PIM 70体积％球形铜粉和30体积％粘合剂的结果。 改变了逐渐改变了大气，以确定逐渐变化对生坯和烧结样品的影响。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号