摘要

Effect of boron addition on structure and mechanical properties of FeAl-WC have been investigated. Elemental powders of iron, aluminum and boron powders have been used as starting materials for MA and mixed to give the desired composition of Fe-40 at% Al +0～5 at% B. Boron addition leads to fine milled powders and improves mechanical properties of Fe-40 at% Al compacts. Milled Fe-40 at% Al powders with 3 at% B have been blended with WC powders and consolidated using pulse current sintering process at 1373 - 1473 K. 3 at% B-added FeAl-SOvol% WC has had high vickers hardness 1230 Hv and transverse rupture strength 1.77 GPa, while no B-added FeAl-5O vol% WC has had 1080 Hv and 1.10 GPa respectively. This is caused by improvement of dispersion of WC paricles in FeAl matrix.
机译：研究了硼添加对Feal-WC结构和机械性能的研究。 铁，铝和硼粉末的元素粉末已被用作MA的起始原料，并混合，得到0％Al + 0〜5的所需组合物，％B.硼加成导致精细研磨的粉末并改善机械性能 Fe-40在％Al紧凑型。 用3at %b的％Al粉末在0％b的％Al粉末与WC粉末混合并在1373-1473KK的脉冲电流烧结过程中混合并在1373-1473k中合并.3，％B加入的Feal-Sovol％WC具有高维氏硬度1230HV 和横向破裂强度1.77 GPA，而B添加的FEAL-5O Vol％WC分别具有1080HV和1.10GPa。 这是由改善WC斑块在Feal基质中的分散来引起的。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号