首页> 外文期刊>Catalysis Communications >Selective photocatalytic carbon dioxide conversion with Pt@Ag-TiO2 nanoparticles
【24h】

Selective photocatalytic carbon dioxide conversion with Pt@Ag-TiO2 nanoparticles

机译：用Pt @ Ag-TiO2纳米粒子选择性光催化二氧化碳转化率

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Pt@Ag-TiO2 nanocomposites were prepared and tested for photocatalytic CO2 conversion in the presence of H2O. The characterizations showed that Pt@Ag core@shell structures were formed. The photocatalytic activity of Pt@Ag-x-TiO2 catalysts with different Ag content showed that the deposition of Ag shell could increase the photocatalytic CO2 reduction efficiency and selectivity by suppressing H-2 generation. Pt@Ag-1.0-TiO2 with an Ag content of 1.95 wt.%s showed a maximum CH4 formation rate of 160.3 mu mol.g(-)(1).h(-1), together with a CO2 reduction selectivity of 87.90%. PL spectra and photocurrent measurements indicated that Pt@Ag-1.0-TiO2 had the highest photogenerated electron-hole separation efficiency among all the prepared photocatalysts.
机译：Pt@Ag-制备了TiO2纳米复合材料，并测试了其在H2O存在下的光催化CO2转化。这些特征表明Pt@Ag core@shell结构形成。光催化活性Pt@Ag-不同银含量的x-TiO2催化剂表明，银壳的沉积可以通过抑制H-2的生成来提高光催化CO2还原效率和选择性。Pt@Ag-Ag含量为1.95 wt.%s的1.0-TiO2显示出最大CH4生成速率为160.3μmol.g（-）（1）。h（-1），以及87.90%的CO2还原选择性。光致发光光谱和光电流测量表明Pt@Ag-在所有制备的光催化剂中，1.0-TiO2的光生电子-空穴分离效率最高。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号