首页> 外文期刊>Journal of Applied Polymer Science >Nafion (R) reinforced with polyacrylonitrile/ZrO(2)nanofibers for direct methanol fuel cell application
【24h】

Nafion (R) reinforced with polyacrylonitrile/ZrO(2)nanofibers for direct methanol fuel cell application

机译：用聚丙烯腈/ ZRO（2）纳米纤维增强Nafion，用于直接甲醇燃料电池施用

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Nafion (R) membrane blended with polyacrylonitrile nanofibers decorated with ZrO(2)was successfully fabricated. The composite membrane showed improved proton conductivity, swelling ratio, thermal and mechanical stability, reduced methanol crossover, and enhanced fuel cell efficiency. The nanocomposite membranes achieved a reduced methanol crossover of 5.465 x 10(-8)cm(2)S(-1)compared to 9.118 x 10(-7)cm(2)S(-1)of recast Nafion (R) membrane using a 5 M methanol solution at 80 degrees C. The composite membrane also showed an ion conductivity of 1.84 compared to 0.25 S cm(-1)recast Nafion (R) at 25 degrees C. The composite membranes showed a peak power density of 68.7 mW center dot cm(-2)at 25 degrees C, these results show a promising composite membrane for fuel cell application.
机译：成功地制备了掺有zro2修饰的聚丙烯腈纳米纤维的Nafion（R）膜。该复合膜显示出改进的质子传导性、溶胀率、热稳定性和机械稳定性、减少甲醇交叉以及提高燃料电池效率。纳米复合膜实现了5.465 x 10（-8）cm（2）S（-1）的甲醇交叉减少，相比之下，在80℃下使用5 M甲醇溶液重铸Nafion（R）膜的甲醇交叉减少了9.118 x 10（-7）cm（2）S（-1）。复合膜还显示了1.84的离子电导率，而在25℃下重铸Nafion（R）膜的离子电导率为0.25 S cm（-1）。复合膜的峰值功率密度为68.7 mW在25摄氏度时，这些结果显示了燃料电池应用的前景。