首页> 外文期刊>Materials and Manufacturing Processes >Processing of copper by keyhole gas tungsten arc welding for uniformity of weld bead geometry
【24h】

Processing of copper by keyhole gas tungsten arc welding for uniformity of weld bead geometry

机译：用钥匙孔钨弧焊加工焊缝几何均匀性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Keyhole gas tungsten arc welding (K-GTAW) was applied to characterize the weld bead geometry in case of the 6 mm thick electrolytic tough pitch copper. Various conditions of welding speeds and preheating on the bead geometry were studied for its uniformity. Visual examination, macro bead dimensional analysis, microhardness profile across the transverse section, microstructural analyses were performed to investigate the K-GTAW on electrolytic tough pitch copper. The results revealed that full penetration of 6 mm can be obtained in a single pass using keyhole mode in GTAW. Keyhole length and width were majorly affected by the welding speed and preheating temperature. Significant variations in weld bead geometry were observed even when high heat input conditions were applied without preheating. Uniform weld bead geometry of 5 mm bead width and depth to width ratio of 0.42 was obtained for a length of 80 mm using appropriate preheating of 300 degrees C and heat input condition of 1.37 kJ/mm (resulted from 300 amperes welding current, 120 mm/min welding speed, and 15.3 volts voltage). In the uniform weld bead geometry, the weld and heat affected zones were consisted of coarse grains relative to base material, wherein the micro hardness variations were observed.
机译：None

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号