首页> 外文期刊>Strength of Materials >Fracture Resistance of Brittle Materials Under Local Loading by Scratching to Edge Chipping. Part. 1. Methodical Grounds of Research
【24h】

Fracture Resistance of Brittle Materials Under Local Loading by Scratching to Edge Chipping. Part. 1. Methodical Grounds of Research

机译：涂抹于边缘碎裂局部装载下脆性材料的断裂抗性。 部分。 1.研究方法

获取原文
获取原文并翻译 | 示例
   

获取外文期刊封面封底 >>

       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Methodical aspects of experimental investigation of brittle materials under local edge loading by scratching the specimen surface with a Rockwell indenter to its edge chipping (S+EF method) are detailed. The edge damage parameter range (fracture distance) had its basis in the literature data on numerical simulation of the stress-strain state in the local indentation zone of the material surface to its edge chipping. Fractographic analysis of tested edges revealed their damage behavior under given loading conditions. The paths of fracture crack propagation to the formation of "shell-like" chip scars, which are asymmetric quasi-conical crack traces, are studied. Partially formed or strained chips having a somewhat distorted fracture surface as compared to the "ideal" geometry of the edge chip were also found. The asymmetry of chip scars was established to have no effect on the fracture resistance of the material. The validity of empirical investigation results was achieved with a minimum test scope, determined by statistical data processing. This test method of low material intensity can be effectively applied to different lines of research.
机译：None

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号