首页> 外文期刊>Journal of Materials Engineering and Performance >Tribological Properties of In Situ-Fabricated NiCr-Al(2)O(3)Composites with SrAl(4)O(7)and SrO at Elevated Temperatures
【24h】

Tribological Properties of In Situ-Fabricated NiCr-Al(2)O(3)Composites with SrAl(4)O(7)and SrO at Elevated Temperatures

机译：在原位制造的NiCr-Al（2）O（3）复合材料的摩擦学性质，其具有SRAL（4）O（7）和升高的温度下的SRO

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The effect of the interaction between SrO and SrAl(4)O(7)with monoclinic and/or orthorhombic structures on the tribological performance of NiCr-Al(2)O(3)composites was evaluated over a wide temperature range. The results indicated that the formation of SrO and SrAl(4)O(7)with monoclinic and/or orthorhombic structures was effective in improving the friction and wear properties of the sintered composites at elevated temperatures. At 400 degrees C, the monoclinic-SrAl4O7, SrO and oxides (NiCr2O4, NiO, and Cr2O3) endowed the sintered composites with low friction coefficient and wear rate. When the temperature was above 600 degrees C, the tribolayer containing monoclinic-SrAl4O7, orthorhombic-SrAl(4)O(7)and oxides exhibited better tribological properties than the tribofilm consisting of monoclinic-SrAl4O7, SrAl(12)O(19)and oxides. Furthermore, at 800 degrees C, the appearance of orthorhombic-SrAl(4)O(7)on the worn surface led to a low friction coefficient and wear rate.
机译：在较宽的温度范围内，研究了单斜和/或正交结构的SrO和SrAl（4）O（7）之间的相互作用对NiCr-Al（2）O（3）复合材料摩擦学性能的影响。结果表明，形成具有单斜和/或正交结构的SrO和SrAl（4）O（7）可以有效地改善烧结复合材料的高温摩擦磨损性能。在400℃时，单斜相SrAl4O7、SrO和氧化物（NiCr2O4、NiO和Cr2O3）赋予烧结复合材料较低的摩擦系数和磨损率。当温度高于600℃时，含有单斜晶SrAl4O7、正交晶SrAl（4）O（7）和氧化物的摩擦层比含有单斜晶SrAl4O7、SrAl（12）O（19）和氧化物的摩擦膜表现出更好的摩擦学性能。此外，在800℃时，磨损表面上出现正交晶态SrAl（4）O（7），导致摩擦系数和磨损率较低。