首页> 外文期刊>Catalysis science & technology >High surface area TiO2-ZrO2 prepared by caustic solution treatment, and its catalytic efficiency in the oxidehydrogenation of para-ethyltoluene by CO2
【24h】

High surface area TiO2-ZrO2 prepared by caustic solution treatment, and its catalytic efficiency in the oxidehydrogenation of para-ethyltoluene by CO2

机译：高表面积TIO2-ZRO2通过苛性溶液处理制备，其在二氧化碳对二甲基二苯二氢化合物中的催化效率通过CO2

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

High surface area TiO2-ZrO2 (1:1) has been synthesized by co-precipitation-digestion method using KOH solution as a hydrolyzing agent as well as a digestion medium. The quenching of the mother liquor solution at elevated temperatures resulted in the amorphization of the TiO2-ZrO2 mixed oxide. The highest surface area obtained for TiO2-ZrO2 by the co-precipitation-digestion method is 256 m~2 g~(-1) calcined at 600 °C with complete amorphous nature and having a particle size of less than 5 nm. Herein, we discuss the concept of amorphization of metal oxides based on the digestion times, supported by the characterization of the catalysts and its application in dehydrogenation of substituted benzene, mainly para-ethyltoluene to para-methylstyrene by CO2 as soft oxidant which showed high conversion and selectivities of 69% and 96%, respectively.
机译：高表面积TIO2-ZRO2（1：1）已通过使用KOH溶液作为水解剂和消化培养基合成了共同饮食方法。 在升高温度下，母液溶液的淬灭导致TiO2-Zro2混合氧化物的非晶化。 通过共凝结消化法为TiO2-Zro2获得的最高表面积为256 m〜2 g〜（-1），在600°C下以完全无定形性质，粒径小于5 nm。 本文中，我们根据消化时间讨论金属氧化物的非晶化概念，并由催化剂的表征及其在取代苯的脱氢作用中的应用，主要是para-乙基苯二酚在para-甲基甲苯中，由CO2作为二氧化碳作为软氧化剂，表现出高度转化的氧化剂。 分别为69％和96％的选择性。