首页> 外文期刊>Catalysis science & technology >NiO microspheres with tunable porosity and morphology effects for CO oxidation
【24h】

NiO microspheres with tunable porosity and morphology effects for CO oxidation

机译：具有可调孔隙率和形态效应的NIO微球以氧化

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Hierarchiral NiO flower-like microspheres with tunable porosity were prepared based on a facile solvothermal method. Three kinds of NiO micro-flowers (NiO-A, NiO-B, and NiO-C) with different porosity have been fabricated mainly by tuning the concentration of nickel nitrate. These flower-like microspheres are comprised of densely packed irregular sheets and display a multi-peaks pore distribution in a wide range in both mesoporous and macroporous regions. The BET surface area of NiO-A, NiO-B and NiO-C is 59.9 m~2 g~(-1), 50.2 m~2 g~(-1) and 15.1 m~2 g~(-1) respectively. The pore volume of NiO-A, NiO-B and NiO-C is 0.2214 cm~3 g~(-1), 0.0829 cm~3 g~(-1) and 0.0549 cm~3 g~(-1), respectively. These NiO spheres show a strong morphology dependant nature for CO oxidation catalysis. Compared to the conventional NiO nanoparticles, these flower-like NiO micro-spheres possess a superior catalytic activity for CO oxidation.
机译：基于便捷的溶剂热法制备了层状尼奥花样微球。 两种具有不同孔隙率的NiO微流（NiO-A，NiO-B和NiO-C）的主要是通过调整硝酸镍的浓度来制造。 这些花样的微球由密集的不规则床单组成，并在介孔和大孔区域中显示了宽范围内的多峰孔分布。 NIO-A，NIO-B和NIO-C的BET表面积分别为59.9 m〜2 g〜（-1），50.2 m〜2 g〜（-1）和15.1 m〜2 g〜（-1） 。 NIO-A，NIO-B和NIO-C的孔体积分别为0.2214 cm〜3 g〜（-1），0.0829 cm〜3 g〜（-1）和0.0549 cm〜3 g〜（-1） 。 这些NIO球体对CO氧化催化的形态依赖性很强。 与常规的Nio纳米颗粒相比，这些花样的Nio微球具有具有优质的催化活性来氧化。

著录项

相似文献

  • 外文文献
  • 中文文献
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号