首页> 外文期刊>Journal of thermal analysis and calorimetry >Interaction of acid and alkali treated titanium with dynamic simulated body environment
【24h】

Interaction of acid and alkali treated titanium with dynamic simulated body environment

机译：Interaction of acid and alkali treated titanium with dynamic simulated body environment

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Interaction of acid and acid+alkali treated titanium samples with simulated body fluid was studied. In case of alkali treated titanium, the dynamic arrangement of the test enabled the detection of primary calcium and phosphate ion adsorption from the solution and later apatite crystal growth (XRD). The induction time for crystal growth was 24.2±0.3 h. On acid-only treated titanium no crystal growth was detected. The calcium phosphate adsorption layer formed on the acid treated samples was detectable by XPS only, however it differed from that one formed on the acid+alkali treated samples. The adsorption layer formed on the acid+alkali treated samples contained larger amount of calcium, especially in the shortest exposure times. Charging of the apatite crystallites during the XPS measurement enabled the determination their Ca/P ratio separately from Ca/P ratio of the adsorption layers. XPS and EDS analyses indicated that the spherulitic crystallites consisted of carbonated hydroxyapatite with the Ca/P ratio close to that one of the stoichiometric hydroxyapatite. It is proposed that the adsorption layer formed spontaneously and immediately on the acid+alkali treated titanium can provide an ideal interface between the metal implant and the apatite cement line, the first structure formed by osteoblast cells during the formation of the new bone on foreign surfaces.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号