首页> 外文期刊>Catalysis Letters >Characterization and Performance of Ca-Substituted La1−xCaxCoO3−δ Perovskite for Efficient Catalytic Oxidation of Toluene
【24h】

Characterization and Performance of Ca-Substituted La1−xCaxCoO3−δ Perovskite for Efficient Catalytic Oxidation of Toluene

机译：Characterization and Performance of Ca-Substituted La1−xCaxCoO3−δ Perovskite for Efficient Catalytic Oxidation of Toluene

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Abstract Perovskite oxides with ABO3 structure are promising heterogeneous catalysts. This work intends to modify the physicochemical properties and catalytic behaviors of perovskite-type oxides by A-site substitution. La1?xCaxCoO3?δ perovskite catalysts with various x?=?0, 0.1, 0.3, 0.5 and 0.7 were prepared and the toluene oxidation performance was investigated. The results show that the calcium substitution increased the surface area, pore volume of the perovskite oxides and the crystal structure was transformed from rhombohedral to cubic symmetry after calcium substitution. Besides, it also changed the surface element composition, low-temperature reducibility and surface oxygen species amounts. 50% of calcium substitution in A-site (La0.5Ca0.5CoO3?δ) was thought to be the optimal content due to the best comprehensive physicochemical properties. The toluene oxidation test verified that the La0.5Ca0.5CoO3?δ presented the best catalytic performance with T50%?=?183?°C and T90%?=?218?°C. The catalytic process was related closely with the rapid transformation of Co2+/Co3+ and the consumption and regeneration of surface adsorbed oxygen. A mechanism of toluene oxidation over La1?xCaxCoO3?δ perovskite was proposed.Graphic Abstract

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号