Bond degradation of rebar and concrete confined with corroded stirrups: effects of concrete grade and casting position

机译：Bond degradation of rebar and concrete confined with corroded stirrups: effects of concrete grade and casting position

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

An experimental study was conducted to investigate the effects of stirrup corrosion, concrete strength and casting position on the behaviour of the bond between steel bars and concrete. Accelerated corrosion was applied to corrode the stirrups in concrete specimens under laboratory conditions. In total, 180 specimens were cast and tested in this experiment. The specimens had three nominal concrete strengths of C20, C40 and C50 with two deformed steel bars of 18 mm in diameter set in a 200 x 200 mm diagonal concrete prism with two stirrups of 8 mm in diameter to provide confinement. The steel bars were cast with different pouring positions, namely the upper and lower ends. Five corrosion levels were investigated, namely 0, 5, 10, 15 and 20%; 12 specimens were investigated for each corrosion level. A pull-out test was carried out to obtain the bond-slip curves. The test results indicate that the porosity of concrete has a great effect on bond degradation with the increase of the steel corrosion level.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号