Based on the reduction law of calcium vanadate, which was explored in the laboratory, the experiments were carried out during direct alloying with calcium vanadate in a high-frequency induction furnace with a capacity of 25 kg. The average recovery ratio of vanadium was 83.4 percent. The tests were also carried out for direct alloying with a briquette of calcium vanadate in a 0.5 t electric arc furnace and with cold-bound pellets of calcium vanadate in a ladle to smelt the low alloy steel with mass contents of about 0.1 percent vanadium. The recovery ratios f vanadium were 89.9 percent and 86.0 percent, respectively.