In vitro Evaluation of Tribocorrosion Induced Failure Mechanisms at the Cell-Metal Interface for the Hip Implant Application

Runa Maria; Lau Eik-lang (Jenny); Takoudis ChristosSukotjo CortinoShokuhfar TolouRocha LuisMathew Mathew

首页> 外文期刊>advanced engineering materials >In vitro Evaluation of Tribocorrosion Induced Failure Mechanisms at the Cell-Metal Interface for the Hip Implant Application

【24h】

In vitro Evaluation of Tribocorrosion Induced Failure Mechanisms at the Cell-Metal Interface for the Hip Implant Application

机译：In vitro Evaluation of Tribocorrosion Induced Failure Mechanisms at the Cell-Metal Interface for the Hip Implant Application

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相关主题

摘要

In a hip joint environment, the bone-metal implant interface of an implant is exposed to the combined effect of wear and corrosion (tribocorrosion). This may create mechanical instability and cause early failure of the implants. The aim of this work was to investigate the tribocorrosion behavior of Ti6Al4V alloys in the presence of bone-forming cells cultured on its surface (cell-metal interface), using an electrochemical and tribological approach. The results showed that at a cathodic potential (-0.9 V), the presence of osteoblast-like cells and serum proteins in the media might induce a higher passivation rate of the oxide film, enhancing the corrosion resistance. However, when the surface is in steady state (0.7 V) they show a lower resistant to corrosion, increasing the susceptibility to corrosion.

著录项

来源
《advanced engineering materials》 |2017年第5期|共16页
作者
Runa Maria; Lau Eik-lang (Jenny); Takoudis ChristosSukotjo CortinoShokuhfar TolouRocha LuisMathew Mathew;
展开▼
作者单位

Rush Univ;

Univ Chicago Illinois;

Univ IllinoisUniv IllinoisUNESP Univ Estadual PaulistaUNESP Univ Estadual Paulista;

展开▼
收录信息
原文格式 PDF
正文语种英语
中图分类
关键词
MELTED TI-6AL-4V ALLOY; COCRMO ALLOY; CORROSION; TI6AL4V; BEHAVIOR; ARTHROPLASTY; EXPRESSION; VIABILITY; WEAR;

In vitro Evaluation of Tribocorrosion Induced Failure Mechanisms at the Cell-Metal Interface for the Hip Implant Application

摘要

著录项

相关主题

期刊订阅