首页> 外文期刊>Corrosion Reviews >Anodic protection of 316L stainless steel piping in sulfuric acid service: failure causes and remedial actions
【24h】

Anodic protection of 316L stainless steel piping in sulfuric acid service: failure causes and remedial actions

机译：Anodic protection of 316L stainless steel piping in sulfuric acid service: failure causes and remedial actions

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Anodic protection (AP) is one of the corrosion control methods that has been widely used in the manufacture, storage, and transport of sulfuric acid. The present paper gives a brief review of the history, some applications, and a case study of failure causes and remedial actions of AP in a sulfuric manufacturing plant. The AP system consists of a direct current source, cathodes, reference electrodes, and signal conditioning electronics. In a sulfuric manufacturing plant, for AP of 316L piping (as an anode), platinized titanium (Pt/Ti) and Hastelloy B-2 were used as reference and cathode electrodes, respectively. After seven years of operation of the AP system in the sulfuric acid plant, a section of the protected pipelines has severely corroded. The study of the system showed that the reference electrodes, which were titanium-electroplated with platinum, lost their stability in the acid with the loss of coating and caused overprotection. However, the system could not control the pipe's potential in the AP situation. In this condition, accelerated corrosion of the cathodes and pipes has also occurred.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号