首页> 外文期刊>Metals and Materials International >High Strength-Elongation Balance in Warm Accumulative Roll Bonded AA1050 Sheets
【24h】

High Strength-Elongation Balance in Warm Accumulative Roll Bonded AA1050 Sheets

机译：High Strength-Elongation Balance in Warm Accumulative Roll Bonded AA1050 Sheets

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Several studies had been performed on accumulative roll bonding (ARB) for AA1050; however, most of them were conducted at room temperature. Here, the ARB process was performed on AA1050 plates through nine cycles at elevated temperature.An innovation introduced a new parameter (UTS×El/ε) to compare the strength-elongation balance between the present studyand previous works. Also, as another parameter, the toughness was compared. Comparing these parameters with previous works showed that the considered samples in the present study performed 14 to 63% better than the other samples, so they were more industrially favorable in terms of mechanical behavior and performance. ARB process at elevated temperature may slightly lead to grain growth compared to room/cryogenic temperature, but creates a better elongation, which ultimately leads to a better balance of the strength-elongation parameter. The results showed that the efect of inter-cycle heating was found signifcant on microstructural evolution and mechanical behavior. Upon fve cycles of the process, the grain size was decreased from 35 to 1.8 μm. The yield strength and ultimate strength increased up to 305% and 94%, respectively. Microhardness test showed that warm ARB reduces inhomogeneity factor in the thickness after 3 cycles. Fractography by SEM showed that the sample failed through shear ductile rupture and that the dimples became smaller, more elongated, and shallower onto the failure surface as the number of ARB cycles increased. In short, the warm process is preferred to the cold process to achieve better mechanical performance and toughness.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号