首页> 外文期刊>Corrosion Reviews >Water-droplet erosion behavior of high-velocity oxygen-fuel-sprayed coatings for steam turbine blades
【24h】

Water-droplet erosion behavior of high-velocity oxygen-fuel-sprayed coatings for steam turbine blades

机译：Water-droplet erosion behavior of high-velocity oxygen-fuel-sprayed coatings for steam turbine blades

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The water-droplet erosion of low-pressure steam turbine blades under wet steam environments can alter the vibration characteristics of the blade, and lead to its premature failure. Using high-velocity oxygen-fuel (HVOF) sprayed water-droplet erosion resistant coating is beneficial in preventing the erosion failure, while the erosion behavior of such coatings is still not revealed so far. Here, we examined the water-droplet erosion resistance of Cr3C2-25NiCr and WC-10Co-4Cr HVOF sprayed coatings using a pulsed water jet device with different impingement angles. Combined with microscopic characterization, indentation, and adhesion tests, we found that: (1) both of the coatings exhibited a similar three-stage erosion behavior, from the formation of discrete erosion surface cavities and continuous grooves to the broadening and deepening of the groove, (2) the erosion rate accelerates with the increasing impingement angle of the water jet; besides, the impingement angle had a nonlinear effect on the cumulative mass loss, and 30 degrees sample exhibited the smallest mass loss per unit area (3) an improvement in the interfacial adhesion strength, fracture toughness, and hardness of the coating enhanced the water-droplet erosion resistance. These results provide guidance pertaining to the engineering application of water erosion protective coatings on steam turbine blades.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号