首页> 外文期刊>journal of the korean ceramic society >Phase evolution, microstructure and dielectric properties of electrospun Ba(Zr0.2Ti0.8)O-3-0.5(Ba0.7Ca0.3)TiO3
【24h】

Phase evolution, microstructure and dielectric properties of electrospun Ba(Zr0.2Ti0.8)O-3-0.5(Ba0.7Ca0.3)TiO3

机译：Phase evolution, microstructure and dielectric properties of electrospun Ba(Zr0.2Ti0.8)O-3-0.5(Ba0.7Ca0.3)TiO3

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Ba(Zr0.2Ti0.8)O-3-0.5(Ba0.7Ca0.3)TiO3 or simply BZT-0.5BCT has attracted increasing attention due to its excellent ferroelectric properties and lack of lead. BZT-0.5BCT nanofibers were fabricated by sol-gel assisted electrospinning and post-calcination process. Different types of analysis were utilized to study phase evolutions and characterization of calcined fibers. TGA indicated three stages of polymer decomposition at temperatures below 500 degrees C. FTIR spectroscopy revealed the presence of acetate salts of inorganic precursors in electrospun fibers. Also, it was determined that the formation of oxides started at temperatures around 300 degrees C and intensified with a rise in temperature. In keeping with DSC and FTIR results, XRD analysis revealed a low crystallization temperature of 550 degrees C for the perovskite phase. The room-temperature Raman spectroscopy demonstrated the coexistence of both orthorhombic and tetragonal phases at 900 degrees C and higher temperatures. SEM images illustrated the stability of fibrous morphology up to 1000 degrees C. High-temperature XRD showed that the curie temperature of nanofibers is between 120 and 150 degrees C. The dielectric constant of calcined fibers at 900 degrees C was measured to be 2283.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号