首页> 外文期刊>Optical Engineering >Characteristic strength, Weibull modulus, and failure probability of fused silica glass
【24h】

Characteristic strength, Weibull modulus, and failure probability of fused silica glass

机译:Characteristic strength, Weibull modulus, and failure probability of fused silica glass

获取原文
获取原文并翻译 | 示例
           

摘要

The development of high-energy lasers has focused attention on the requirement to assess the mechanical strength of optical components made of fused silica or fused quartz (SiO_(2)). The strength of this material is known to be highly dependent on the stressed area and the surface finish, but has not yet been properly characterized in the published literature. Recently, Detrio and collaborators at the University of Dayton Research Institute (UDRI) performed extensive ring-on-ring flexural strength measurements on fused SiO_(2) specimens ranging in size from 1 to 9 in. in diameter and of widely differing surface qualities. We report on a Weibull statistical analysis of the UDRI data--an analysis based on the procedure outlined in Proc. SPIE 4375, 241 (2001). We demonstrate that (1) a two-parameter Weibull model, including the area-scaling principle, applies; (2) the shape parameter (m approx= 10) is essentially independent of the stressed area as well as the surface finish; and (3) the characteristic strength (1-cm~(2) uniformly stressed area) obeys a linear law, (sigma)_(C) (in megapascals) approx-160-2.83 X PBS (in parts per million per steradian), where PBS characterizes the surface/subsurface "damage" of an appropriate set of test specimens. In this light, we evaluate the cumulative failure probability and the failure probability density of polished and superpolished fused SiO_(2) windows as a function of the biaxial tensile stress, for stressed areas ranging from 0.3 to 100 cm~(2).

著录项

获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号