Dynamic Recrystallization Mechanism and Precipitation Behavior of Mg-6Gd-3Y-3Sm-0.5Zr Alloy During Hot Compression

机译：Dynamic Recrystallization Mechanism and Precipitation Behavior of Mg-6Gd-3Y-3Sm-0.5Zr Alloy During Hot Compression

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The effects of temperature and strain on dynamic recrystallization (DRX) and dynamic precipitation of Mg-6Gd-3Y-3Sm-0.5Zr alloy were studied through uniaxial compression. The main conclusions were as follows: the increase of strain or temperature can promote DRX. The texture strength decreases with the increase of DRX fraction. The pyramidal slip and pyramidal slip were activated to coordinate strain when deformed at high-temperature. Under the deformation condition of T = 400 degrees C, (epsilon) over dot = 0.002 s(-1) and epsilon = 0.35, the mechanism of DRX was mainly discontinuous dynamic recrystallization. The rotation continuous dynamic recrystallization gradually becomes the main mechanism with the increase of strain and temperature. At the same time, the particle stimulated nucleation (PSN) caused by a single large-sized Mg-5(Gd, Y, Sm) or the aggregation of multiple Mg-5(Gd, Y, Sm) phases was also found. The dynamic precipitation can stimulate the nucleation of DRX, and the boundary of DRXed grains can become an effective nucleation site for dynamic precipitation. DRX and dynamic precipitation can promote nucleation mutually.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号