Corrosion performance of a corrosion-resistant rail steel in the simulated subsea tunnel environment

机译：Corrosion performance of a corrosion-resistant rail steel in the simulated subsea tunnel environment

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The corrosion performance of a newly developed corrosion-resistant rail steel (U68CuCr) was investigated and compared with that of a normally used high-speed rail steel (U71MnG) by neutral salt spray tests, electrochemical tests, X-ray diffraction analyses, and the scanning vibrating electrode technique. It was found that the weight loss and corrosion rate of U68CuCr were lower than those of U71MnG under the same corrosion conditions. In addition, due to the influence of alloying elements (copper and chromium) in U68CuCr, the rust layer was thicker and denser, resulting in a stronger protective effect. Moreover, U68CuCr had a higher corrosion potential in electrochemical tests. Finally, the dynamic corrosion process of U68CuCr in 2.2% NaCl solution mainly followed a lateral extension of corrosion. Therefore, the corrosion resistance of U68CuCr was better than that of U71MnG in the subsea tunnel environment.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号