首页> 外文期刊>Nanotechnology >Fabrication and characterization of well-ordered PbS nanowires in aluminum oxide template by sulfurization and vacuum injection molding processes
【24h】

Fabrication and characterization of well-ordered PbS nanowires in aluminum oxide template by sulfurization and vacuum injection molding processes

机译：Fabrication and characterization of well-ordered PbS nanowires in aluminum oxide template by sulfurization and vacuum injection molding processes

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Abstract Lead (Pb) nanowire arrays were fabricated with anodic aluminum oxide (AAO) templates of 30, 100 and 300 nm in pore diameters. Through vacuum injection molding process, Pb/AAO composite was obtained, and lead sulfide (PbS) could further be synthesized after exposing to sulfur gas. AAO templates with different pore sizes were fabricated by using pure aluminum in a two-step anodization. Three types of solutions, which are 10 vol% sulfuric acid, 3 wt% oxalic acid and 1 vol% phosphoric acid, were adopted to achieve AAO of various pore sizes. Different sulfurization temperatures and time spans were applied for studying on the formation mechanism of PbS. Finally, the morphology, composition, structure and elements distribution of the as-prepared Pb and PbS nanowires were confirmed through the use of scanning electron microscopy, energy dispersive x-ray spectroscopy, element-mapping, x-ray diffraction and transmission electron microscopy analysis. The results indicated that Pb nanowires were successfully obtained after applying vacuum injection molding process with 50 kgf cm−2 hydraulic pressure, and PbS nano arrays can be formed by sulfurization at 500 °C for 5 h. Furthermore, an optical property, ultraviolet–visible (UV–Vis) absorption, was also measured. The measurement of the PbS nanowires showed that a significant quantum confinement effect made the energy gap produce a blue shift from 0.41 eV to 1.65 eV or 1.72 eV.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号