Mechanical behaviour of porous kaolin-based ceramics for potential catalysts support applications

机译：Mechanical behaviour of porous kaolin-based ceramics for potential catalysts support applications

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

In this study, porous kaolin-based ceramic support materials were successfully fabricated using conventional sintering techniques. The support materials were prepared using two different weight per cent (wt.%) of sawdust addition (10-20 wt.%), compacted at 10-20 MPa and sintered at 900 and 1000 degrees C. The physical and mechanical properties of the support materials as formed by sintering were examined, while the failure rate of the fabricated support materials was determined using Weibull statistical tool. The experimental data show that the best result for the hardness and fracture toughness was obtained as 0.409 GPa and 0.835 MPa.m(1/2) for supports sintered at 1000 degrees C with 20 wt.% pore formers. The mass loss for the support materials with the best properties was reported to be about 5%, making the support a potential material for use as catalyst support. The Weibull modulus (m) obtained for the ceramic support was in a range of 2.75-4.00, indicating that the samples had a lower failure rate than most ceramic support materials with a Weibull modulus of more than 6. The control samples and samples with the inclusion of pore formers demonstrated acoustic emission (AE) response during the entire cooling process during the acoustic emission test.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号