首页> 外文期刊>Advanced functional materials >The Evolution of Photoluminescence Properties of PEA_2SnI_4　Upon Oxygen Exposure: Insight into Concentration Effects
【24h】

The Evolution of Photoluminescence Properties of PEA_2SnI_4　Upon Oxygen Exposure: Insight into Concentration Effects

机译：The Evolution of Photoluminescence Properties of PEA_2SnI_4　Upon Oxygen Exposure: Insight into Concentration Effects

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The time evolution of the photoluminescence properties in phenylethylammonium tin halide perovskite (PEA(2)SnI(4)) film as a function of oxygen concentration is reported. Photo-brightening and reversible photoluminescence quenching are observed in PEA(2)SnI(4) film at ultralow oxygen concentration ( 1.5 vol%). In the case of 1.5 vol% [O-2] 21 vol%, the photoluminescence emission of PEA(2)SnI(4) film can be partially recovered after resetting the samples to nitrogen box. As the oxygen concentration further increases with the range of 21 to 95 vol%, the photoluminescence emission of PEA(2)SnI(4) film is significantly quenched and can only be slightly recovered after removing it to the nitrogen box. By correlating the material characterizations and theoretical analysis, the interactions between PEA(2)SnI(4) and oxygen contain physisorption and chemical reactions are illustrated. Depending on the oxygen concentration, the chemical reactions between PEA(2)SnI(4) and oxygen can be reversible and/or irreversible. The insights into oxygen concentration effects provide a guideline to optimize the stability of PEA(2)SnI(4) for achieving high-performance optoelectronic devices.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号