首页> 外文期刊>ISIJ International >Effect of N Content on Precipitated Phase and Long-term Aging Stability of 9CrMoCoB Steel
【24h】

Effect of N Content on Precipitated Phase and Long-term Aging Stability of 9CrMoCoB Steel

机译：Effect of N Content on Precipitated Phase and Long-term Aging Stability of 9CrMoCoB Steel

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Microstructure observation and hardness analysis of 9CrMoCoB steel with different N content during long-term aging at 620 degrees C were carried out by Thermo-Calc thermodynamic calculation, scanning electron microscope, transmission electron microscope and hardness test. The results show that the average size of M23C6 phase increases first with the extension of aging time, then stabilizes after aging for 2 000 h, and decreases gradually with the increase of N content. The Laves phase precipitated after aging for 1 000 h and coarsened continuously with the aging time prolonging. The coarsening rate tended to be flat after 2 000 h. The average size of Laves phase decreased gradually with the increase of N content. With the increase of N content, the average diameter and unit number of BN inclusions increase gradually, and the unit number of BN inclusions larger than 2 mu m increases obviously when N content is 0.025% and 0.030%. The hardness of 9CrMoCoB steel decreases gradually with the aging time and tends to be stable after aging for 2 000 h. With the increase of N content, the hardness and stability of 9CrMoCoB steel first increase and then decrease, and both reach the maximum when N content is 0.020%. Considering comprehensively, in order to give full play to the strengthening effect of B and N in steel and improve the properties and stability of 9CrMoCoB steel, the optimal control range of N content in steel is around 0.020%.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号