首页> 外文期刊>journal of the korean ceramic society >Thermal plasma arc discharge method for high-yield production of hexagonal AlN nanoparticles: synthesis and characterization
【24h】

Thermal plasma arc discharge method for high-yield production of hexagonal AlN nanoparticles: synthesis and characterization

机译：Thermal plasma arc discharge method for high-yield production of hexagonal AlN nanoparticles: synthesis and characterization

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Large scale with high-purity hexagonal aluminum nitride nanoparticles (AlN NPs) was synthesized using DC thermal plasma arc discharge method (TPAD). Argon gas was used as the plasma forming gas, while ammonia (NH3) gas was used as the reactive gas, which was fed into the reactor at a constant flow rate of 5 LPM. In order to optimize the process for high yield, the experiments were carried out at various plasma input powers, such as 1.5, 3.0, and 4.5 kW. Following the optimization, to examine the influence of using pure nitrogen gas, an experiment was also carried out in the nitrogen ambience. The phase identification and structural determination of the synthesized NPs were carried out using XRD and Raman spectroscopic analyses. While the morphology, particle size, and elemental compositions of the synthesized NPs were observed from SEM, HRTEM, XPS, and EDX analyses. The photoluminescence response was confirmed from the PL spectrum. The PL emission peaks observed around 440 nm (2.8 eV) and 601 nm (2.07 eV), respectively, which correspond to the UV blue and red band emissions of both AlN and Al/AlN NPs. The results show that the synthesized nano-AlN NPs exhibit excellent crystallinity with a high yield of approximately 210 g/h. The current plasma technology can be regarded as a perfect potential process for developing nano-AlN powders with improved efficiency.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号